The Fe-Pd ferromagnetic shape memory alloy is a multifunctional material. We investigated the behavior of the superelastic properties of rapidly solidified Fe-Xat%Pd (X=29.3, 29.6, 30.2 and 30.4) alloy ribbons to develop biomedical materials applicable to orthodontics and medical instrumentation. The appearance of a stress-induced martensite phase under the loading stress was confirmed by X-ray diffraction measurements. Stress-strain curves were drawn from results obtained using a tensile testing machine at temperature of 290 and 313 K. The Fe-Xat%Pd (X=29.6, 30.2, 30.4) ribbons exhibited superelastic strain of 3.0–3.5%. Moreover, when these Fe-Pd alloy ribbons were treated in Hanks’ solution for 150 days, they exhibited good biocorrosion resistance.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 49 (2), 360-364, 2008
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679227419520
-
- NII論文ID
- 10021144335
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 9354712
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可