Microstructual Characterization of Sputtered Pt–Ir Coatings on Ni-Base Single Crystal Superalloy
-
- Suzuki Aya
- Thermal Spray Group, Materials Engineering Laboratory, National Institute for Materials Science
-
- Harada Masanori
- Undergraduate Student, Department of Materials Engineering, Graduate School of Engineering, the University of Tokyo
-
- Wu Yingna
- Thermal Spray Group, Materials Engineering Laboratory, National Institute for Materials Science
-
- Murakami Hideyuki
- Thermal Spray Group, Materials Engineering Laboratory, National Institute for Materials Science
Bibliographic Information
- Other Title
-
- Microstructual Characterization of Sputtered Pt–Ir Coatings on Ni-Base Single Crystal Superalloy
Search this article
Description
Characterization of Pt–Ir alloy coatings on a Ni-base single crystal superalloy was carried out. Pt–Ir alloys with varied composition were sputter-deposited on TMS-82+, which were then subjected to annealing and Al-pack cementation treatments. It was found that all the as-deposited films consisted of Pt–Ir solid solutioned fcc single phase, while the annealing treatment at 1423 K for 1 h drastically changed the microstructure, depending on the composition of coated layers. On the other hand, concentration profiles of alloying elements were not drastically changed by the Al-pack cementation process. It was also revealed that Ir addition increases the surface hardness of all the as-deposited, annealed, and aluminized specimens.
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 46 (8), 1760-1763, 2005
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282679227500672
-
- NII Article ID
- 130004823894
-
- NII Book ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2MXhtFSnt7rM
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 7402669
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed