Mechanical Properties of Newly Developed Age Hardenable Mg-3.2 mol%Gd-0.5 mol%Zn Casting Alloy
-
- Ozaki Tomomichi
- Materials Department Research Laboratory, IHI Corporation
-
- Kuroki Yasunori
- Materials Department Research Laboratory, IHI Corporation
-
- Yamada Kentaro
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- Hoshikawa Hiroaki
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- Kamado Sigeharu
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- Kojima Yo
- Department of Mechanical Engineering, Nagaoka University of Technology
この論文をさがす
抄録
A new Mg-Gd-Zn-base cast alloy was developed for high strength casting products. Effects of Zn content on microstructures and tensile strength were investigated. Both Mg-3.2%Gd-0.5%Zn-0.2%Zr (in mol%, 0.5GZ) and Mg-3.2%Gd-0.75%Zn-0.2%Zr (0.75GZ) alloys showed remarkable age hardening by precipitation of β′ phase with bco structure as similar to Mg-Gd-Y-Zr alloy. The precipitates are finer and denser than those of Mg-Gd-Y-Zn-Zr alloy by Zn and a large amount of Gd addition. Mg3Gd compound particles remained at grain boundaries after solution treatment. Long period stacking ordered (LPSO) phase did not form. It is considered that Mg3Gd particles suppressed grain coarsening during the heat treatment, and provided fine grain structure of about 30 μm in diameter. Tensile strength of the T6-treated 0.5GZ alloy was 410 MPa at room temperature and the high strength was kept by 473 K.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 49 (10), 2185-2189, 2008
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679227507968
-
- NII論文ID
- 10024325673
- 130004453779
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 9663107
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可