Microstructural control of the TiO2-SnO2 binary system and synthesis of SnO2 nanowhiskers by micro wave irradiation

DOI Web Site Web Site 被引用文献4件 参考文献61件 オープンアクセス
  • Aoyagi Takuya
    Department of Applied Chemistry, Graduate School of Engineering, Tohoku University
  • Hayashi Yamato
    Department of Applied Chemistry, Graduate School of Engineering, Tohoku University
  • Takizawa Hirotsugu
    Department of Applied Chemistry, Graduate School of Engineering, Tohoku University

書誌事項

タイトル別名
  • Microstructural Control of the TiO<SUB>2</SUB>-SnO<SUB>2</SUB> Binary System and Synthesis of SnO<SUB>2</SUB> Nanowhiskers by Microwave Irradiation

この論文をさがす

説明

SnO2 single crystals (columnar crystals and silver grass-like nanowhiskers) were synthesized by selective microwave heating of a TiO2-SnO2 mixture. The shape of the as-grown SnO2 crystals is strongly dependent on the atmosphere during microwave irradiation. This is due to the difference in growth mechanisms, as revealed by in-situ surface observation under microwave irradiation, in addition to scanning and transmission electron microscopy observations of irradiated specimens. In a N2 atmosphere, silver grass-like SnO2 nanowhiskers were obtained. On the other hand, columnar SnO2 crystals were obtained in air or an O2 atmosphere. Photoluminescence and absorption spectra of the as-grown SnO2 crystals were examined. Based on the analysis of a TiO2-SnO2 pellet, it was found that the bottom was selectively heated, and SnO2 sublimated by microwave irradiation. A density gradient texture of the sample pellet was formed.