Electron Irradiation Induced Crystallization of the Amorphous Phase in Zr-Cu Based Metallic Glasses with Various Thermal Stability
-
- Nagase Takeshi
- Department of Materials Science and Engineering, Graduate School of Engineering, & Handai Frontier Research Center, Osaka University
-
- Umakoshi Yukichi
- Department of Materials Science and Engineering, Graduate School of Engineering, & Handai Frontier Research Center, Osaka University
この論文をさがす
説明
The phase stability of the amorphous phase against electron irradiation and the crystallization behavior under electron irradiation were investigated in Zr-Cu based metallic glasses. The phase stability of the amorphous phase against thermal crystallization, i.e., thermal stability was evaluated by the temperature range of supercooled liquid region (ΔTx). The ΔTx values for Zr66.7Cu33.3, Zr65.0Al7.5Cu27.5 and Zr65.0Al7.5Ni10.0Cu17.5 alloys were 54K, 89K and 119K, respectively. The amorphous phase of Zr-Cu based metallic glasses was not stable under electron irradiation. The crystallization of fcc-Zr2Cu phase was accelerated by electron irradiation instead of bct-Zr2Cu phase which appeared during thermal annealing. The increase in the thermal stability of the amorphous phase is effective for the decrease in the crystallization rate under electron irradiation, but not always effective in suppressing the occurrence of electron irradiation induced crystallization.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 45 (1), 13-23, 2004
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679227913216
-
- NII論文ID
- 10011981472
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2cXhtFKru7g%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6824832
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可