Influence of Frequency on the High-Temperature Fatigue Crack Growth Behavior of 17-4 PH Stainless Steels
-
- Hsu Kuei-Chang
- Department of Mechanical Engineering, National Central University
-
- Lin Chih-Kuang
- Department of Mechanical Engineering, National Central University
この論文をさがす
説明
The influence of frequency on fatigue crack growth (FCG) behavior was investigated for three differently heat-treated 17-4 PH stainless steels, namely unaged “Condition A,” peak-aged “Condition H900,” and overaged “Condition H1150,” at 673 and 773 K, and at frequencies ranging from 0.002 to 20 Hz. At 773 K, all heat-treated conditions exhibited similar FCG behavior in which no frequency effect was observed at frequencies higher than 2 Hz and the fatigue crack growth rates (FCGRs) increased with decreasing frequency below 2 Hz. The increase in FCGR at a lower frequency at 773 K was thought to be caused by a time-dependent, oxidation-assisted cracking mechanism. At 673 K, for a given heat-treated condition, the FCGRs increased with decreasing frequency at higher frequencies and leveled off at lower frequencies. Such an anomalous FCG behavior was attributable to a dynamic strain aging (DSA) effect. At a given frequency, when the temperature was increased from 673 to 773 K, the FCGR increased in Condition H1150, but decreased in Conditions A and H900 due to an in-situ overaging and precipitate-coarsening effect during the FCG test for the latter.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 48 (3), 490-499, 2007
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679228076032
-
- NII論文ID
- 130004453493
- 10018734928
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8671118
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可