In-Situ Observation and Acoustic Emission Analysis for SCC of MgCl₂ Droplet in SUS304 Stainless Steel

書誌事項

タイトル別名
  • <i>In-Situ</i> Observation and Acoustic Emission Analysis for SCC of MgCl<sub>2</sub> Droplet in SUS304 Stainless Steel

この論文をさがす

抄録

Acoustic emission and optical video microscope monitoring was proposed to investigate the stress corrosion cracking of work-hardened SUS304 stainless steel caused by a small magnesium-chloride droplet. The crack propagation length could measure clearly under the droplet by VMS. The SCC started at 45–82 ks with pitting. The crack velocity was 3.2–4.7 µm/ks and it propagated almost continuously. AE signals were generated at early stage of SCC testing of 55 and 82 ks, after that they were generated discontinuously. With the SEM observations, the detected AE signals were mainly attributed to cracking of the oxidation products and discontinuous crack propagation at the falling-off surface grain.

収録刊行物

被引用文献 (6)*注記

もっと見る

参考文献 (11)*注記

もっと見る

関連プロジェクト

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ