Effect of Precipitation of σ-Phase and N Addition on the Mechanical Properties in 25Cr–7Ni–4Mo–2W Super Duplex Stainless Steel

DOI Web Site Web Site 被引用文献1件 参考文献22件 オープンアクセス
  • Kim Soo-Cheon
    Division of Materials Science & Engineering, Pukyong National University
  • Zhang Zuogui
    Dept. of Functional Machinery & Mechanics, Shinshu University
  • Furuya Yuji
    Dept. of Functional Machinery & Mechanics, Shinshu University
  • Kang Chang-Yong
    Division of Materials Science & Engineering, Pukyong National University
  • Sung Jang-Hyun
    Division of Met. & Che. Eng., Dong-A University
  • Ni Qing-Qing
    Dept. of Functional Machinery & Mechanics, Shinshu University
  • Watanabe Yoshimi
    Dept. of Functional Machinery & Mechanics, Shinshu University
  • Kim Ick-soo
    Dept. of Functional Machinery & Mechanics, Shinshu University

書誌事項

タイトル別名
  • Effect of Precipitation of σ-Phase and N Addition on the Mechanical Properties in 25Cr–7Ni–4Mo–2W Super Duplex Stainless Steel
  • Effect of Precipitation of シグマ Phase and N Addition on the Mechanical Properties in 25Cr 7Ni 4Mo 2W Super Duplex Stainless Steel

この論文をさがす

説明

This study was carried out to investigate the effects of precipitation of σ phase and N addition and the change of volume fraction on the mechanical properties in 25Cr–7Ni–4Mo–2W super duplex stainless steel. The results obtained from this study are as follows: With increasing the annealing temperature, the volume fraction of austenite increased while volume fraction of ferrite decreased. Volume fraction of austenite was found to be increased by N addition. Tensile strength decreased and elongation increased due to increasing the volume fraction of austenite by increasing annealing temperature. In the case of specimens with N addition, tensile strength and elongation showed high values. σ phase was formed at ferrite phase and interface of ferrite and austenite. More precipitation of σ phase was stimulated by N addition.<BR>With increasing volume fraction of precipitated σ phase, tensile strength was increased, while elongation and impact value decreased. In the case of σ phase precipitated specimen (with N addition), tensile strength, elongation, hardness and impact values showed higher values than those without N addition. It was also found that impact value rapidly decreases in early stage of aging.