Mechanically Induced Solid-State Reaction for Synthesizing New Multicomponent Ta55Zr10Ni10Al10Cu15 Glassy Alloy Powders with Extremely Wide Supercooled Liquid Region
-
- El-Eskandarany M. Sherif
- Inoue SuperLiquid Glass Project, Exploratory Research for Advanced Technology,Japan Science and Technology Corporation
-
- Zhang Wei
- Inoue SuperLiquid Glass Project, Exploratory Research for Advanced Technology,Japan Science and Technology Corporation
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Mechanically Induced Solid-State Reaction for Synthesizing New Multicomponent Ta<SUB>55</SUB>Zr<SUB>10</SUB>Ni<SUB>10</SUB>Al<SUB>10</SUB>Cu<SUB>15</SUB> Glassy Alloy Powders with Extremely Wide Supercooled Liquid Region
この論文をさがす
抄録
New multicomponent Ta-based glassy alloy powder was synthesized by mechanical alloying a mixture of elemental Ta55Zr10Ni10Al10Cu15 powders at room temperature, using a low-energy ball mill. The glassy powders of the final-product (1080 ks) in which its glass transition temperature (Tg) lies at a high temperature (834 K), crystallize through a single sharp exothermic peak at 1004 K (Tx). The total enthalpy change of crystallization (ΔHx) is −10.32 kJ/mol. The supercooled liquid region before crystallization (ΔTx) of the synthesized glassy powder shows the widest value (170 K) of any reported metallic glassy system.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (6), 1422-1425, 2002
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679228361472
-
- NII論文ID
- 10012324653
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD38Xls1Siurc%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6200932
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可