Effects of Pulse Current on an Aluminum Powder Oxide Layer During Pulse Current Pressure Sintering
-
- Nagae Takekazu
- Central Research Institute, Toyama Industrial Technology Center
-
- Yokota Masaru
- Takaoka National College
-
- Nose Masateru
- Takaoka National College
-
- Tomida Shogo
- Central Research Institute, Toyama Industrial Technology Center
-
- Kamiya Takashi
- Faculty of Engineering, Toyama University
-
- Saji Shigeoki
- Faculty of Engineering, Toyama University
この論文をさがす
抄録
The pulse current pressure sintering and hot press process were applied for sintering of aluminum powder produced by water and gas atomizing methods. The pulse current pressure sintering process could densify the water atomized powder in a short time compared with the hot pressing because it could remove the H2 gas at lower temperature. The gas prevents sintering of aluminium powder. The tensile strength of the pulse current pressure sintered gas atomized powder which contains low H2 was higher than that of hot pressed specimen. The electric resistivity of sintered specimens obtained by pulse current pressure sintering process was lower than that of hot pressed specimen. The oxide layer destruction was confirmed by this measurement of electric resistivity. The oxide layers were supposed to be fractured by the high temperature region which is attributed to Joule heat by contact resistance.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (6), 1390-1397, 2002
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679228362752
-
- NII論文ID
- 10012324529
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD38Xls1Siur0%3D
-
- ISSN
- 13475320
- 13459678
- http://id.crossref.org/issn/09161821
-
- NDL書誌ID
- 6200812
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可