Al₀.₅TiZrPdCuNi High-Entropy (H-E) Alloy Developed through Ti₂₀Zr₂₀Pd₂₀Cu₂₀Ni₂₀ H-E Glassy Alloy Comprising Inter-Transition Metals
-
- Takeuchi Akira
- WPI-Advanced Institute for Materials Research, Tohoku University
-
- Wang Junqiang
- WPI-Advanced Institute for Materials Research, Tohoku University
-
- Chen Na
- WPI-Advanced Institute for Materials Research, Tohoku University
-
- Zhang Wei
- Institute for Materials Research, Tohoku University School of Materials Science and Engineering, Dalian University of Technology
-
- Yokoyama Yoshihiko
- Institute for Materials Research, Tohoku University
-
- Yubuta Kunio
- Institute for Materials Research, Tohoku University
-
- Zhu Shengli
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Al<sub>0.5</sub>TiZrPdCuNi High-Entropy (H-E) Alloy Developed through Ti<sub>20</sub>Zr<sub>20</sub>Pd<sub>20</sub>Cu<sub>20</sub>Ni<sub>20</sub> H-E Glassy Alloy Comprising Inter-Transition Metals
この論文をさがす
抄録
An Al0.5TiZrPdCuNi high-entropy (H-E) alloy with a bcc single phase was found through a Ti20Zr20Pd20Cu20Ni20 H-E glassy alloy designed based on equi-atomicity inherent to H-E alloys. The constituent elements and the composition of the Ti20Zr20Pd20Cu20Ni20 alloy were determined by regarding a binary Cu64Zr36 bulk metallic glass as Cu60Zr40 alloy and subsequent replacements of the Cu and Zr atoms with other late- and early-transition metals, respectively. The Ti20Zr20Pd20Cu20Ni20 alloy in a ribbon shape forms into a glassy single phase. The addition of 0.5Al to the Ti20Zr20Pd20Cu20Ni20 H-E glassy alloy resulted in forming a bcc single phase for a rod specimen with a diameter of 1.5 mm. The analysis revealed that the Al0.5TiZrPdCuNi H-E alloy is characterized by mixing enthalpy of −46.7 kJ·mol−1 and Delta parameter of 8.8, which are considerably larger and negative for the former and larger for the latter against the conventional H-E alloys.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 54 (5), 776-782, 2013
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679228582912
-
- NII論文ID
- 10031168425
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC3sXhtFChs7fN
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 024457093
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可