Examination of the Tensile Deformation Resistance and Ductility of Friction Stir Processed Al-Cu 2218 Alloy at Elevated Temperatures
-
- Chen Ssu-Ta
- Department of Materials Science and Engineering, National Cheng Kung University
-
- Lui Truan-Sheng
- Department of Materials Science and Engineering, National Cheng Kung University
-
- Chen Li-Hui
- Department of Materials Science and Engineering, National Cheng Kung University
この論文をさがす
抄録
Tensile properties dependence of elevated testing temperatures (100°C∼450°C) on as extruded and as friction stir processed Al-Cu 2218 alloy were investigated. The tensile deformation resistance of an as friction stir processed sample is higher than an as extruded one as increased testing temperature up to 300°C and this is a consequence of natural aging effect. However, the tensile deformation resistance decreased evidently as the testing temperature raised to 400°C∼450°C, meanwhile there was a concomitant improvement of tensile ductility due to a homogeneously grain refinement which facilitated a pronounced grain boundary sliding in this temperature range.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 51 (8), 1474-1480, 2010
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679228586624
-
- NII論文ID
- 10026513777
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 10769008
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可