Pseudo-Superplastic Characteristics of ZK60 Alloy with Fibrous Microstructure
-
- Wang Cheng-Yu
- Department of Materials Science and Engineering, National Chao Tung University
-
- Wang Jian-Yih
- Department of Materials Science and Engineering, National Dong Hwa University
-
- Saufan Akhmd
- Department of Materials Science and Engineering, National Dong Hwa University
-
- Fu Yen-Pei
- Department of Materials Science and Engineering, National Dong Hwa University
この論文をさがす
抄録
<p>The superplasticity of ZK60 alloy was investigated after thermomechanical treatments (combination of rolling at 473 K and 673 K). ZK60 alloy, with an equiaxial grains microstructure (average grain size 2.6 µm), showed a maximum elongation of 865.2% with the strain rate 1 × 10−4 s−1 under high temperature tensile test at 573 K. Surprisingly, hot-rolled ZK60 samples with fibrous microstructure also displayed pseudo-superplastic behavior with an elongation of 535.2% at the same temperature. Microstructures indicated that the hot-rolled samples with elongated grains exhibited dynamic recovery and recrystallization during high temperature deformation, transforming the fibrous to fine-grained crystals, and thus retaining pseudo-superplastic behavior.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 59 (4), 674-678, 2018
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679228846464
-
- NII論文ID
- 130006549539
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 028918645
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可