Effect of Ag Addition to Zn22 mass%Al-2 mass%Cu Alloy on the Four-Phase Reaction η + ε → α + τ'
-
- Dorantes-Rosales H.J.
- Instituto Politécnico Nacional, ESIQIE-ESFM, Ciudad de México
-
- López-Hirata V.M.
- Instituto Politécnico Nacional, ESIQIE-ESFM, Ciudad de México
-
- Hernández-Santiago Felipe
- Instituto Politécnico Nacional, ESIQIE-ESFM, Ciudad de México
-
- Saucedo-Muñoz M.L.
- Instituto Politécnico Nacional, ESIQIE-ESFM, Ciudad de México
-
- Paniagua-Mercado Ana María
- Instituto Politécnico Nacional, ESIQIE-ESFM, Ciudad de México
書誌事項
- タイトル別名
-
- Effect of Ag Addition to Zn22 mass%Al–2 mass%Cu Alloy on the Four-Phase Reaction η + ε → α + τ′
この論文をさがす
抄録
<p>The effect of Ag additions to the four-phase, η + ε → α + τ′, was studied experimental and thermodynamically using Zn–22 mass%Al–2 mass%Cu base alloys with four Ag contents from 0 to about 4 mass% Ag. SEM and XRD results indicated the presence of the τ′ phase decreased as the Ag content increased for the aged alloys which can be attributed to the stabilization of the ε phase because of its increase in Ag content which is in agreement with Thermo-Calc results. The Ag addition also promoted a slowest decrease in hardness in the aging curves at 200°C which can be attributed to the slowest diffusion process for the quaternary alloy.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 59 (5), 717-723, 2018
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679229281408
-
- NII論文ID
- 130006725823
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 028962905
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可