Interface Magnetic Anisotropy of Pd/Co₂Fe[x]Mn₁₋xSi/MgO Layered Structures
-
- Kubota Takahide
- Institute for Materials Research, Tohoku University
-
- Kamada Tomonari
- Institute for Materials Research, Tohoku University
-
- Kim Jinhyeok
- Institute for Materials Research, Tohoku University
-
- Tsukamoto Arata
- Department of Electronic Engineering, Nihon University
-
- Takahashi Shigeki
- Samsung R&D Institute Japan
-
- Sonobe Yoshiaki
- Samsung R&D Institute Japan
-
- Takanashi Koki
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Interface Magnetic Anisotropy of Pd/Co<sub>2</sub>Fe<i><sub>x</sub></i>Mn<sub>1−<i>x</i></sub>Si/MgO Layered Structures
この論文をさがす
抄録
Interface magnetic anisotropy of Co2FexMn1−xSi Heusler alloy thin films were studied quantitatively. Films of Co2MnSi (x = 1, CMS), Co2Fe0.5Mn0.5Si (x = 0.5, CFMS), and Co2FeSi (x = 1, CFS) were fabricated onto MgO (001) substrates with an epitaxially grown Pd (001) under layer, and were capped by an MgO layer. The maximum thickness for the perpendicular magnetization was 0.8 nm for CMS and CFMS, and it was 0.6 nm for CFS. The interface anisotropy energies (Ks) were 1.5, 1.5, and 1.2 erg/cm2 for CMS, CFMS, and CFS, respectively. The difference in Ks probably originated from the different alloying conditions at the bottom interface between Pd and Co2FexMn1−xSi layers.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 57 (6), 773-776, 2016
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679229681536
-
- NII論文ID
- 130005153161
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 027330970
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可