Effect of a High Static Magnetic Field on the Origin of Stray Grains during Directional Solidification
-
- Zhong Hua
- State Key Laboratory of Advanced Special Steel, Shanghai University
-
- Li Chuanjun
- State Key Laboratory of Advanced Special Steel, Shanghai University
-
- Wang Jiang
- State Key Laboratory of Advanced Special Steel, Shanghai University
-
- Ren Zhongming
- State Key Laboratory of Advanced Special Steel, Shanghai University
-
- Zhong Yunbo
- State Key Laboratory of Advanced Special Steel, Shanghai University
この論文をさがす
抄録
<p>The formation of stray grains in directionally solidified Al-4.5 mass% Cu alloy under an axial high static magnetic field up to 6 T has been investigated. Electron backscattering diffraction (EBSD) was performed to analysis the orientation of the stray grains. The experimental results suggest that the formation of the stray grains are significantly affected by the external magnetic field. The modification of dendrite morphology demonstrates the existence of thermoelectric magnetic effect on dendrite scale. It is implied that the thermoelectric magnetic force (TEMF) gives rise to the pinch-off of the sidebranches. When the fragments form, they will become the souce of the stray grains. Moreover, free dendritic fragment will rotate in melt and tend to align the 〈310〉 crystallographic axis along the direction of the magnetic field. This is because of the magnetic torque induced by the anisotropic susceptibility of α-Al crystal.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 57 (8), 1230-1235, 2016
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679230055168
-
- NII論文ID
- 130005165724
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 027512322
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可