The Effects of Anodization Treatment on the Microstructure and Fatigue Behavior of 7075-T73 Aluminum Alloy
-
- Shih Teng-Shih
- Department of Mechanical Engineering, National Central University
-
- Lee Tin-Hou
- Department of Mechanical Engineering, National Central University
-
- Jhou Ying-Jhe
- Department of Mechanical Engineering, National Central University
この論文をさがす
抄録
The fatigue behaviors of 7075-T73 alloy with/without anodization/sealing treatment were investigated in this study. The microstructure of different samples was analyzed by electron microscopy. As the experiments, the microstructure were observed from the anodized/sealed samples to indicate that precipitates trapped at subsurface near film/metal (f/m) interface would partly dissolved and the deformed matrix existed high fractions of high angle grain boundaries. The bare 7075-T73 alloy samples achieved fatigue strength of 225 MPa and the anodized/sealed samples enhanced their fatigue strength at 107 life cycles with 10–20 µm film thickness. The fractured anodized/sealed sample showed fine striation spacing than bare sample after subjected to low stress amplitude.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 55 (8), 1280-1285, 2014
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679230393344
-
- NII論文ID
- 130004825210
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 025617296
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可