紡機用焼結リングの材質設計と性能評価　（第２報）　耐摩耗特性について

DOI

書誌事項

タイトル別名
  • Material Design and Performance Evaluation of Porous Sintered Metal Ring for Spinning Frame. Part 2. Abrasive Resistance.
  • Part 2 : Abrasive Resistance
  • (第2報) 耐摩耗特性について

抄録

In this report, a study was made on the influence which the compound ratio of sintering annexes MOS2 and FeMn contained in porous sintered metal has on the characteristics of wear resistance of iron-based porous sintered metal ring, with a view to improving the wear resistance characteristics of spinnig ring.First, we specified 5 different kinds of compound ratio and conducted abrasion tests to check the relationship among compound ratio, amount of wear, surface roughness and gas permeability of ring.According to test results, the best characteristics of waer resistance were obtained when the compound ratio of MoS2in the sintering annexes was 60∼67%.Next, this newly developed ring (66.7% MoS2, 33.3% FeMn) and conventional standard ring (100% MoS2) were submitted to actual load operation and the changes of amount of wear, gas permeability and surface roughness of both rings against the operating time were measured and compared with each other. From the results of this experiment, it has been found that the former is superior to the latter in wear resistance characteristics and that this superioirty comes from the fact that the pores of the newly developed ring are shaped in way to better lubricate the ring surface.

収録刊行物

  • 繊維機械学会誌

    繊維機械学会誌 49 (2), T36-T48, 1996

    一般社団法人 日本繊維機械学会

キーワード

詳細情報 詳細情報について

  • CRID
    1390282679241958912
  • NII論文ID
    130004391310
  • DOI
    10.4188/transjtmsj.49.t36
  • ISSN
    18801994
    03710580
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • Crossref
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ