Effects of Structural Isomerism and Precursor Structures on Thermo-optic Coefficients of BPDA/PDA Polyimide Films
-
- Matsumura Akiko
- Department of Organic & Polymeric Materials, Tokyo Institute of Technology
-
- Terui Yoshiharu
- Department of Organic & Polymeric Materials, Tokyo Institute of Technology
-
- Ando Shinji
- Department of Organic & Polymeric Materials, Tokyo Institute of Technology
-
- Abe Akira
- Materials Science, Toyohashi University of Technology
-
- Takeichi Tsutomu
- Materials Science, Toyohashi University of Technology
この論文をさがす
抄録
The effects of the structural isomerism and the alkyl side-chain lengths in the precursors of BPDA/PDA polyimide (PI) on the temperature dependence of the refractive indices (i.e. thermo-optical coefficients) have been investigated. The PIs were formed on Si substrates by thermal curing of a) poly(amic acid)s (PAA) derived from three isomers (s-, a-, and i-) of biphenyltetracarboxylic acid dianhydride (BPDA) and p-di-minobenzene (PDA) and b) poly(amide alkylester)s (PAEs) having methyl-, n-propyl-, n-pentyl-, and n-octyl side chains. The TO coefficients of PIs increase as the average refractive indices and thermal expansion coefficients increase, which can be well explained with the derivative form of the Lorentz-Lorenz formula. The absolute values of TO coefficients for s-BPDA/PDA are smaller than those expected from their refractive indices, which is due to the dense molecular packing and the small coefficient of thermal expansion. Significantly larger TO coefficients were observed for the PI films prepared from PAEs than that from PAA, indicating that the larger volatile components (alcohols) eliminated during thermal imidization cause loose molecular packing in the former PIs. The use of structural isomers and chemical modification of precursors are effective to control the TO coefficients and their anisotropies in BPDA/PDA films.
収録刊行物
-
- Journal of Photopolymer Science and Technology
-
Journal of Photopolymer Science and Technology 20 (2), 167-174, 2007
フォトポリマー学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679300810368
-
- NII論文ID
- 130004464521
- 40015602470
-
- NII書誌ID
- AA11576862
-
- COI
- 1:CAS:528:DC%2BD2sXot1WntLw%3D
-
- ISSN
- 13496336
- 09149244
-
- NDL書誌ID
- 8918759
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可