Effects of Density and Heat Treatment Temperature on Wear Performance of C/C Composites.
-
- MIYAUCHI Toru
- Railway Technical Research Institute
-
- TSUJIMURA Taro
- Railway Technical Research Institute
-
- MURATA Kiyoshi
- Faculty of Technology, Shibaura Institute of Technology
-
- SHINJYO Akira
- Ohwada Carbon Industry Co., Ltd.
Bibliographic Information
- Other Title
-
- C/Cコンポジットの密度や最終焼成温度が摩耗特性に及ぼす影響
- C C コンポジット ノ ミツド ヤ サイシュウ ショウセイ オンド ガ マモウ トクセイ ニ オヨボス エイキョウ
Search this article
Abstract
High-speed frictional tests of C/C composites having different densities and the final heat treatment temperatures have been studied. It was found that the wear resistance of C/C composites expressed by the number of tests increased with the increase of the densities at heat treatment temperatures (HTT) 1873 and 2273K, while this value decreased at HTT 2473K when the density was high. It was confirmed from the analysis of the experimental results that the best value for wear resistance of C/C composites was obtained at the average atomic face lattice distance d(002) was 0.339 to 0.340nm.
Journal
-
- Materials life
-
Materials life 12 (2), 98-102, 2000
MATERIALS LIFE SOCIETY, JAPAN
- Tweet
Details 詳細情報について
-
- CRID
- 1390282679314897280
-
- NII Article ID
- 10004660776
-
- NII Book ID
- AN10530609
-
- ISSN
- 21857024
- 09153594
-
- NDL BIB ID
- 5384235
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- CiNii Articles
-
- Abstract License Flag
- Disallowed