ポリ塩化ビニル／ポリウレタン　ブレンドの熱劣化

DOI

書誌事項

タイトル別名
  • Thermal degradation of blends of poly (vinyl chloride)/polyurethane.

説明

Thermal degradation of blends of Poly (vinyl chloride) /Polyurethane (PVC/PU) was examined by thermogravimetry, differential thermal analyis, ultraviolet-visible spectroscopy, measurement of gel content and chemiluminescence analysis. The results obtained were as follows : Thermal degradation of the blends started at lower temperatures than that of each homopolymer. Polyene formation of PVC caused by HCI elimination reaction and successive gel formation by crosslinking reaction were accelerated by the blend of PU, and maximum effect was observed at 1 I blend ratio (wt) Relative amount of chemiluminescence of PU due to thermal oxidation was reduced remarkably by the blend of PVC. Thus, thermal degradation of the each component polymer in the blends was accelerated by the other component.

収録刊行物

詳細情報 詳細情報について

  • CRID
    1390282679316203904
  • NII論文ID
    130003792530
  • DOI
    10.11338/mls1989.2.232
  • ISSN
    21857024
    09153594
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ