- Basic Characteristic of Milled Fiber made from waste FRP-derived glass fibers
- 廃FRP由来ガラス繊維を原料としたミドルファイバーの基本的特性
- ハイFRP ユライ ガラス センイ オ ゲンリョウ ト シタ ミドルファイバー ノ キホンテキ トクセイ
この論文をさがす
抄録
This study clearly introduces the basic characteristics of milled fiber made from waste FRP-derived glass fibers through depolymerization of unsaturated polyester under ambient pressures.It was found that the waste FRP-derived glass fibers were 25 mm in length with a cotton-like texture. The ratio of aim range (100-300 μm) of the milled fiber was provided by two phases of the processes that changed the distance of the grinder was higher than that of the existing article.Milled fiber made from waste FRP-derived glass fiber maintained resin and calcium carbonate, however the fiber of the existing article did not have resin and calcium carbonate. It was found that the degree of crystalline of the composite material made from waste FRP-derived glass fiber and post-consumer PET (polyethylene telephthalate) bottle was at the same level as the material existing article and post-consumer PET bottle and only PET bottle. Moreover, the sample which compounded showed strength of 1.5 times of the no composition and the tensile strength of the plastic which compounded with the milled fiber from waste FRP-derived glass fibers was higher than that of the existing article.
収録刊行物
-
- 素材物性学雑誌
-
素材物性学雑誌 23 (2), 38-42, 2011
日本素材物性学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679321125376
-
- NII論文ID
- 110008680232
-
- NII書誌ID
- AN10140273
-
- COI
- 1:CAS:528:DC%2BC3MXhtFGnsbfF
-
- ISSN
- 18846610
- 09199853
-
- NDL書誌ID
- 11203689
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可