- Binderless Fabrication of Composite Derived from Rice Husk and Carbon Fiber Ends and its Mechanical Properties
- モミガラ ト タンソ センイ ハザイ ニ ユライ スル フクゴウ ザイリョウ ノ バインダレス セイゾウ ト ソノ リキガク トクセイ
この論文をさがす
説明
A carbon/silica/carbon-fiber composite (CSCFC) was fabricated from agricultural waste of rice husk (RH) and industrial waste of carbon fiber (CF) ends. The powder-state RH mixed with chopped CF ends (0 to 30mass%) was molded into a disk by means of hot-pressing in an inert condition without using any binders, and then heated to 500 and 1000°C. Mechanical properties of CSCFC and the role of CF addition level on them were evaluated. The CSCFC added with 10 mass% of CF and heated to 500°C displayed the highest compressive strength of 61 MPa. It was also shown that higher heat treatment temperature reduced the compressivestrength. The CF restricted a uniform thermal shrinkage of the matrix material derived fromRH, causing cracks and eventually reducing the compressive strength. The friction coefficient atthe CSCFC surface was evaluated under a contact with a SUS304 ball. The CSCFC added with CF at 20mass% and heated to 1000°C displayed the lowest kinetic friction coefficient of 0.12. The CSCFC produced from waste materials of RH and CF ends were shown to have high compressive strength and low friction coefficient even if they were fabricated without using any binders.
収録刊行物
-
- 素材物性学雑誌
-
素材物性学雑誌 24 (1_2), 1-6, 2012
日本素材物性学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679323048448
-
- NII論文ID
- 130003377332
-
- NII書誌ID
- AN10140273
-
- ISSN
- 18846610
- 09199853
-
- NDL書誌ID
- 023601083
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- KAKEN
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可