Effect of functional monomers with phosphorus on bonding durability to high-purity titanium

  • YANAGIDA Hiroaki
    Department of General Dentistry, Nagasaki University Hospital of Medicine and Dentistry
  • TANOUE Naomi
    Specialized Dentistry, Nagasaki University Hospital of Medicine and Dentistry
  • ATSUTA Mitsuru
    Division of Fixed Prosthodontics and Oral Rehabilitation, Nagasaki University Graduate School of Biomedical Sciences
  • KOISHI Yoshikazu
    Department of Dental Materials, Nihon University School of Dentistry at Matsudo
  • MATSUMURA Hideo
    Department of Prosthodontics, Nihon University School of Dentistry

Bibliographic Information

Other Title
  • リン含有機能性モノマーが高純度チタンの接着耐久性に及ぼす影響

Search this article

Abstract

The purpose of the current study was to evaluate the effect of functional monomers with phosphorus on bonding durability to titanium. Three metal conditioners (Alloy Primer, AP; Metal Link, ML; Eyesight Opaque Primer, EP) were assessed. The functional monomers for base metal are 10-methacryloyloxydecyl dihydrogenphosphate (MDP) for the AP, 6-methacryloxyhexyl phosphonoacetate (MHPA) for the ML, and methacrylatephosphate (MP) for the EP. Cast disk specimens made of high-purity titanium (T-Alloy H) were air-abraded with 70μm alumina, primed with three conditioners, and then bonded with an acrylic resin adhesive (Super-Bond C&B). Shear bond strengths were determined both before and after thermocycling (20, 000 cycles).<BR>Before thermocycling, the shear bond strengths for the AP and ML groups were significantly higher than those for the EP and unprimed (defined as control) groups (p<0.05). The AP group exhibited significantly higher bond strength than the ML group after thermocycling (p<0.05). Significant difference was not found between the EP and the unprimed groups regardless of thermocycling application (p>0.05).

Journal

  • Adhesive Dentistry

    Adhesive Dentistry 22 (2), 97-102, 2004

    Japan Society for Adhesive Dentistry

Citations (1)*help

See more

References(19)*help

See more

Details 詳細情報について

Report a problem

Back to top