- タイトル別名
-
- Solvothermal Synthesis of ITO Nanoparticles and Their Application to the Transparent Conductive Film
- ITO ナノ リュウシ ノ ソルボサーマル ゴウセイ ト トウメイ ドウデンマク エ ノ オウヨウ
この論文をさがす
説明
Indium tin oxide (ITO) nanoparticles have been synthesized from the mixed ethylene glycol solution of indium (III) chloride, tin (II) chloride and sodium hydroxide by the solvothermal process with the addition of oleylamine or oleic acid as a protective reagent. The x-ray diffraction patterns of particles synthesized at 250°C show that the ITO begins to be produced after the reaction duration of 6 h when oleylamine is added to the reaction solution, indicating a promoting effect on the ITO formation, whereas only indium oxyhydroxide is formed when oleic acid is used. The transmission electron microscopic observation has revealed that ITO nanoparticles obtained by the addition of oleylamine are monodisperse and their size increases from 4-5 nm to 50-60 nm with elongating reaction duration from 6 to 96 h. ITO thin films are prepared by the multiple deposition of a collodion membrane incorporating synthesized ITO nanoparticles on the glass substrate followed by sintering at 400-500°C. They exhibit a good transparency in the visible region and a specific resistivity as low as 1.0 Ω·cm.<br>
収録刊行物
-
- 高圧力の科学と技術
-
高圧力の科学と技術 22 (2), 129-134, 2012
日本高圧力学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679357768960
-
- NII論文ID
- 10030642214
-
- NII書誌ID
- AN10452913
-
- COI
- 1:CAS:528:DC%2BC38Xht1SgtbfJ
-
- ISSN
- 13481940
- 0917639X
-
- NDL書誌ID
- 023819966
-
- 本文言語コード
- ja
-
- 資料種別
- journal article
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可