- Kume H.
- Technology Research Institute of Osaka Prefecture
-
- Nishikawa Y.
- Technology Research Institute of Osaka Prefecture
-
- Inamura S.
- Technology Research Institute of Osaka Prefecture
-
- Miyamoto H.
- Technology Research Institute of Osaka Prefecture
-
- Yamabe K.
- Kyocera Corporation
-
- Maeda T.
- Kyocera Corporation
書誌事項
- タイトル別名
-
- Strengthening of Al2O3-ZrO2 Composites by HIP Sintering.
- Strengthening of Al2O3-ZrO2 Composite b
この論文をさがす
抄録
Al2O3-ZrO2 (95/5 wt%a) composite powders have been prepared by the coprecipitation technique. Both normal sintering and capsule-free HIP sintering have been performed under various sintering conditions. The combination of normal sintering at 1798 K and HIP sintering at 1723 K enhances the bending strength of the composites to 958 MPa. Bending strength above 1 GPa is succeeded by capsule HIPing at 1623 K. The enhancement of bending strength is discussed in connection with the sintering conditions.
収録刊行物
-
- 高圧力の科学と技術
-
高圧力の科学と技術 7 1087-1089, 1998
日本高圧力学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679359142272
-
- NII論文ID
- 10002692896
-
- NII書誌ID
- AN10452913
-
- ISSN
- 13481940
- 0917639X
-
- NDL書誌ID
- 4494155
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可