- Comparative study of impact fatigue with usual fatigue.
- コウ ノ ショウゲキ ヒロウ ト ツウジョウ ヒロウ ノ ヒカク ケンキュウ
この論文をさがす
抄録
Impact Fatigue and usual fatigue experimenls were carried out by using carbon steel and high-manganese steel specimens. Impact fatigue lives for crack initiation at the notch roots and for fracture were unfavorable compared with usual fatigue. Although crack propagating periods under pulsated and repeated loadings were comparable in the case of usual fatigue, difference of such a loading condition influenced on both crack initiation and propagation period in the case of impact fatigue. According to the result of measuring of the dislocation density in terms of the Xray method, plastic zone size near a crack was estimated to be small in the case of impact fatigue compared with that of usual fatigue. Similar results were obtained for high manganese steel, and the influence of rolling direction was not observed.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 56 (525), 1051-1057, 1990
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679395482112
-
- NII論文ID
- 110002373090
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3668703
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可