In order to achieve the objective of securing the reliability of high-temperature components, it is necessary to establish a method for predicting the remaining life of their materials subjected to severe creep-fatigue damage. It was reported by the authors that multiple small cracks initiated along grain boundaries on the specimen surface at the very early stage of life in creep-fatigue and their growth and coalescence formed the main crack which induced the failure. Moreover, the process of small crack initiation and growth showed random behavior due to microstructural inhomogeneity. A stochastic model was proposed and the failure process was numerically simulated by means of the Monte Carlo method. This paper provides a scheme of the small-crack-simulation-method for the evaluation of remaining life of the materials in high-temperature components, which is an integration of our previous studies and is summarized in a flow chart.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 57 (540), 1732-1737, 1991
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679395544832
-
- NII論文ID
- 110002370677
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3726489
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可