- Effect of Compressive Prestress on the Mechanical Properties of Isotropic Graphite.
- トウホウセイ コクエン ノ リキガク トクセイ ニ オヨボス アッシュク ヨオ
この論文をさがす
抄録
Compressive prestresses were applied to isotropic fine-grained graphite at room temperature (RT) and high temperature (2010°C). As a result, decrease in Young's modulus due to high-temperature prestressing was 56% which was much larger than the 6.4% that was due to RT prestressing. This finding was considered to be due primarily to difference in degree of preferred orientation of crystallites in the graphite on the basis of Bacon anisotropy factor (BAF) from X-ray diffraction measurement of the prestressed specimens. Furthermore, high-temperature compressive prestressing produced an increase in the strength of the isotropic graphite, although room temperature prestressing produced no such effect. The results obtained here suggest that isotropic graphite which is subjected to high-temperature compressive stress becomes anisotropic.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 61 (590), 2185-2189, 1995
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679423189376
-
- NII論文ID
- 110002378095
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3640445
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可