Rotating bending fatigue tests were carried out for an 18%Ni maraging steel to investigate the effect of shot peening on the fatigue strength. The fatigue strength increased markedly by the shot peening. The increase in the fatigue strength due to the shot peening depended on the shot size and the stress level. Fracture mode changed from the surface fracture in the short life region to the interior fracture i. e. fish-eye fracture in the long life region. And in the middle life region, both cracks initiated from the surface and the inside of material in dividually coalesced and lead to the final fracture. These results were discussed from the effect of shot size on the surface roughness and the depth and magnitude of compressive residual stress and work hardening.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 65 (639), 2267-2273, 1999
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679423190144
-
- NII論文ID
- 110002375160
-
- NII書誌ID
- AN0018742X
-
- COI
- 1:CAS:528:DC%2BD3cXhtVClurc%3D
-
- ISSN
- 18848338
- 03875008
- http://id.crossref.org/issn/03875008
-
- NDL書誌ID
- 4921256
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可