- Relationship between Fatigue Limit of Austenitic Stainless Steels and Existence of Micro-cracks.
- オーステナイトケイ ステンレス コウ ノ ヒロウゲン ト ビシ キレツ ノ ソンザイ ニ カンケイ スル ケンキュウ
この論文をさがす
説明
Fatigue tests have been performed to investigate the effect of strain aging on the fatigue limit and fatigue crack behavior about two kinds of austenitic stainless steels, SUS 304 and nitrogen contained SUS 304 (SUS 304 N). From the testing results, the fatigue limits of SUS 304 and SUS 304 N increase by 5 and 30 MPa, respectively by the low temperature annealing (300°C×2h) during fatigue test by the specified cyclic ratio under constant higher stress amplitude than their original fatigue limits. It is considered that the effect of strain aging by nitrogen in SUS 304 N increases its fatigue limit. However, the specimens, in which the fatigue micro-cracks in the length of 1∼2 grains sizes exist under the higher stress amplitude than the fatigue limit of each material, propagate to be a final fracture before 1×107 cycles under the same original stress amplitude of fatigue limit, even if the specimens were annealed in the vacuum at low temperature.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 65 (631), 656-661, 1999
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679423750656
-
- NII論文ID
- 110002374929
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 4692539
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可