ＳＵＳ３０４の軸力疲労特性に及ぼすひずみ時効および過大応力の影響

DOI Web Site Web Site 被引用文献1件 参考文献10件

書誌事項

タイトル別名
  • Effect of Strain Aging and Overstress on Fatigue Property of SUS 304.
  • SUS 304 ノ ジクリョク ヒロウ トクセイ ニ オヨボス ヒズミ ジコウ オヨビ カダイ オウリョク ノ エイキョウ

この論文をさがす

抄録

Axial cyclic tension-compression fatigue test has been performed about the typical austenitic stainless steel (SUS 304) using a servo-controlled electro-hydraulic fatigue tester. The main object of this study is to investigate the effect of strain aging and overstress on fatigue property of SUS 304, which is applied just after fatigue micro-crack initiation. The main results obtained in this study are summarized as follows : (1) The effect of strain aging on fatigue property which has not been observed in high cycle rotating bending fatigue test, is obviously recognized in low cycle axial compression-tension test. (2) The fatigue life (σa=300MPa) is enhanced 211.1 times by the combination of overstress and aging treatment. The reason concerning in this outstanding effect is that, strain aging does play a much more significant role for improving the fatigue strength besides the strain hardening and austenite-martensite transformation caused by overstress. (3) Non-propagating fatigue micro-crack is observed in the specimen, which has been suffered under the stress amplitude of fatigue limit by 1×107 cycles, with combining overstress (525MPa, 50 sec) with aging treatment (350°C×2hrs).

収録刊行物

被引用文献 (1)*注記

もっと見る

参考文献 (10)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ