- Environmentally Assisted Cracking of Low Alloy Steel under Cyclic Straining. 1st Report. Effect of Strain Wave Form on the Acceleration of Crack Initiation and Propagation.
- テイゴウキン コウ ノ ヘンドウ ヒズミカ ノ カンキョウ ジョチョウ ワレ ダイ1ポウ キレツ ハッセイ デンパ ノ カソク ニ エイキョウ スル ヒズミハケイ インシ
この論文をさがす
抄録
Environmentally assisted cracking tests were performed using 3.5 NiCrMoV low alloy steel in deionized water containing 100 ppb dissolved oxygen at 333K. Effects of strain rate, strain hold time and superposed vibratory stress on crack initiation and propagation were investigated. Slower strain rate, longer strain hold time and larger superposed vibratory stress enhanced damage and resulted in shorter life. Effect of each factor on the reduction of life was obtained. The crack morphology was transgranular and widened by corrosion.
収録刊行物
-
- 日本機械学会論文集Ａ編
-
日本機械学会論文集Ａ編 65 (629), 174-179, 1999
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679423829632
-
- NII論文ID
- 110002374860
-
- NII書誌ID
- AN0018742X
-
- COI
- 1:CAS:528:DyaK1MXitVarsbY%3D
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 4640812
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可