- Effect of Temperature on Fatigue Properties of GFRP under Tension/Torsion Biaxial Loading.
- ヒッパリ ネジリ 2ジク カジュウ カ ニ オケル ヒラオリ GFRP ノ ヒロウ トクセイ ニ オヨボス シケン オンド ノ エイキョウ
この論文をさがす
抄録
The effect of temperature on fatigue properties of a plain weave glass fabric reinforced plastics(GFRP)under tension/ torsion biaxial loading was studied. Fatigue tests were conducted at several terperatures between -23 and 60°C. The biaxial loads were proportinally applied to specimens. Although the static strength of GFRP at elevated terperature was lower than that at room and low terperatures below 0°C, the fatigue life at 60°C was longest when the specimens were subjected to a tension/torsion biaxial stress combination whose maximum cyclic stress normalized by the static strength at each temperature was constant for all tests.The primary fatigue damage at elevated temperature was meta-delamination occurring at cross-over points between wefts and warps. No meta-delamination was observed in the specimens tested at temperatures below 0°C while matrix cracks propagating across fiber bundles were formed. The modulus decay of GFRP in shear was greatly influenced by internal fatigue damage such as meta-delamination and matrix cracking more than the modulus decay in tension.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 66 (651), 2049-2054, 2000
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679423900032
-
- NII論文ID
- 110002373354
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 5574767
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可