小球押込みによるセラミックスの強度低下に関する研究　窒化けい素に対する窒化けい素球押込み―弾性応答を仮定した場合

DOI Web Site Web Site 被引用文献6件 参考文献20件

書誌事項

タイトル別名
  • Strength Degradation in Ceramics by Sphere Indentation. Si3N4 Sphere Indentation of Si3N4 Specimen-Case of Elastic Condition.
  • ショウ キュウ オシコミ ニヨル セラミックス ノ キョウド テイカ ニカンス

この論文をさがす

抄録

Indentation tests on silicon nitride specimens using a silicon nitride sphere were carried out in order to establish a method for evaluating sphere indentation or impact damage of surface layers and post-indentation residual strength in structural ceramics. The residual strengths of indented specimens were measured by four-point bending tests. The relationship between indentation load and cone crack length was derived from the equilibrium condition of cone crack. Then the residual strength was estlmated from the cone crack length. The estimated values were in good agreement with the was estimated from the cone crack length. The estimated values were in good agreement with the measured values. only in the region of low indentation load where elastic deformation is dominant.

収録刊行物

被引用文献 (6)*注記

もっと見る

参考文献 (20)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ