- Low-Cycle Fatigue Properties of High Manganese Content Steel.
- コウ マンガン コウ ノ テイ サイクル ヒロウ トクセイ
この論文をさがす
抄録
Fatigue tests in the low-cycle range had been performed to investigate the fatigue crack initiation characteristics under a completely reversed push-pull load. The material used in this test is high manganese content austenitic steel (HM steel) in comparison with a typical austenitic stainless steel SUS304. Then, it is confirmed that there are no differences in the fatigue crack initiation and the relatively small crack growth properties, and that the Manson-Coffin law can be applied to these two kinds of materials. In addition, the gradient in the relationship between the plastic strain and the number of cycles under the strain-controlled condition becomes larger for HM steel than that for SUS304. On the other hand, HM steel shows the same properties as SUS304 in the relation between the cumulative plastic strain and the number of cycles to failure not only under the strain-controlled condition but also under the stress-controlled condition.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 61 (582), 211-216, 1995
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679424003072
-
- NII論文ID
- 110002372225
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3601641
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可