Evaluation of Surface Damage and Residual Strength in Ceramics due to Sphere Impact. 1st Report, Si3N4 Sphere Impact to Si3N4 Specimen-Experinrental Results.

DOI Web Site Web Site 4 Citations 22 References

Bibliographic Information

Other Title
  • 小球衝突によるセラミックスの表面損傷と残留強度の評価　第１報　　窒化けい素平板への窒化けい素球衝突‐実験結果
  • ショウキュウ ショウトツ ニ ヨル セラミックス ノ ヒョウメン ソンショウ ト ザンリュウ キョウド ノ ヒョウカ 1 チッカ ケイソ ヘイバン エ ノ チッカ ケイソキュウ ショウトツ ジッケン ケッカ

Search this article

Abstract

In order to clarify mechanisms of surface damage and to establish methods for evaluating strength degradation in ceramics subjected to impact of solid particles, testings of silicon nitride sphere impact to silicon nitride specimens were carried out. The residual strengths of specimens were measured by flexural tests, in which the damaged surfaces were the tensile sides. Fractures were classified to several types depending on their own impact damages. Influences of specimen thickness on the impact damage and the residual strength were also examined. From the comparison of test results of indentation and impact, the possibility was shown that the residual strength due to sphere impact would be evaluated using a method based on the elastic indentation theory.

Journal

Citations (4)*help

See more

References(22)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top