- Characteristics of Small Crack Growth in a Nickel-Base Superalloy.
- Niキ チョウゴウキン ノ ビショウ キレツ デンパ トクセイ
この論文をさがす
抄録
Rotating bending fatigue tests were carried out for Inconel 718 at room temperature to investigate the growth characteristics of a small crack. It was found that : (1) The crack initiated at the grain boundary and then propagated as a transgranular crack. (2) When the stress level was higher than the fatigue limit, the fatigue life was mainly controlled by the growth life of a crack smaller than 1mm. (3) The fatigue limit was a limiting stress for the crack propagation. (4) At low stress levels (σa/σ0.2<0.5, σa : stress amplitude, σ0.2 : 0.2% proof stress), the crack growth rate was determined by the stress intensity factor range ΔK ; and at high stress levels (σa/σ0.2>0.6), it was determined by the small crack growth law.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 63 (611), 1398-1402, 1997
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679424297728
-
- NII論文ID
- 110002374182
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 4265502
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可