円孔を有する平織りＧＦＲＰの引張り／ねじり組合せ荷重下における疲労に関する研究　第１報　疲労強度と損傷進展過程

DOI Web Site Web Site

書誌事項

タイトル別名
  • Fatigue Damage Evaluation of a Circular Hole-Notched GFRP under Tension-Torsion Biaxial Loading. 1st Report, Fatigue Strength and Damage Process.
  • エンコウ オ ユウスル ヒラオリ GFRP ノ ヒッパリ ネジリ クミアワセ

この論文をさがす

抄録

Fatigue strength and the failure process of a hole-notched glass FRP under tension-torsion biaxial cyclic loading were investigated in this paper. Thin cylindrical specimens were used. Fibers of the reinforcement (plain woven glass cloth) were aligned parallel to the longitudinal and circumferential axes of the specimen. The damage state at each biaxial stress ratio (α : the ratio of normal stress to shear stress) was observed macroscopically and microscopically. The experiments reveal the following results. The fatigue damage progression is dependent on the biaxial stress ratio. When α=1/0, damage spreads radially from the hole, but only covers an area of π/4 to either side of the circumferential axis, in both directions along the circumferential axis. When α=0/1, damage progresses radially along both longitudinal and circumferential axes. We call each of these a "fatigue band". Under biaxial loading, macroscopic and microscopic damage states have both types of damage at α=1/0 and α=0/1.

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ