- Crack Forming Developed at Sharp Notch Bottom in Relation to Fatigue Reliability at Elevated Temperature for Advanced Carbon Fiber-Reinforced Thermal Plastics.
- センシン CFRTP ノ コウオン ヒロウ シンライセイ ニ カカワル スルド
この論文をさがす
抄録
The estimation of fatigue reliability at elevated temperatured for advanced carbon fiber reinforced PA46 was examined. Especially meso crack forming stage developed on notch bottom and its effect on fatigue reliability at elevated temperature. The main results are as follows, (1) The fatigue strenght, life of crack initiation and life of crack propagation for V-notch specimens were almost the same at elevated temperature. (2) From fractography using SEM, it was recognized that the matrix was elongated and the cementing of the interface between fiber and matrix was poor. So it was thought that the crack propagation resistance at elevated temperature was not influence by the kinds of fiber. (3) It was considered that the difference of crack tip heat change accompanying fatigue damage and crack propagation was controlled under the linear fracture mechanics.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 63 (608), 695-701, 1997
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679425553920
-
- NII論文ID
- 110002374079
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 4203161
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可