過酸化物添加によるポリ（Ｌ‐乳酸）の成形加工性の改良

DOI Web Site 参考文献24件

書誌事項

タイトル別名
  • The Improvement of Plastic Processability of Poly (L-Lactic Acid) Modified by Dicumyl Peroxide
  • カサンカブツ テンカ ニ ヨル ポリ L ニュウサン ノ セイケイ カコウセイ ノ カイリョウ

この論文をさがす

抄録

GPC and rheological measurements under shear and uniaxial flow for Poly (L-lactic acid) modified by dicumyl peroxide were carried out. The description of experimental GPC resulted that some amounts of added dicumyl peroxide caused an increase of cross-linked regions in the polymer. The viscoelastic properties of poly (L-lactic acid) modified by dicumyl peroxide under the shear flow were investigated. It was found that the rheological properties of the poly (L-lactic acid) were distinctly different from those of a neat poly (L-lactic acid). The elastic response at low frequencies was significantly enhanced in comparison with the neat poly (L-lactic acid). Uniaxial elongation behavior was also measured. In short time region, the elongational viscosity of Poly (L-lactic acid) modified by dicumyl peroxide were three times larger than the shear viscosity. This result meant that Trouton's rule is applicable to the results. Beyond a certain critical strain, the uniaxial elongational viscosity showed rapid increase, which was referred to as strain hardening. Die-swell ratio increased with dicumyl peroxide contents. Furthermore poly (L-lactic acid) modified by dicumyl peroxide was molded by direct-blow. The thickness distribution could be homogeneous by modified peroxide.

収録刊行物

  • 成形加工

    成形加工 14 (9), 598-603, 2002

    一般社団法人 プラスチック成形加工学会

参考文献 (24)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ