せん断溶融混練が気相成長炭素繊維/ポリカーボネート複合体の電気伝導性に与える影響

DOI Web Site Web Site 参考文献30件 オープンアクセス

書誌事項

タイトル別名
  • Effect of Melt Mixing on Electrical Conductivity of Vapor Grown Carbon Fiber/Polycarbonate Composites
  • センダン ヨウユウコンレン ガ キソウ セイチョウ タンソ センイ ポリカーボネート フクゴウタイ ノ デンキ デンドウセイ ニ アタエル エイキョウ

この論文をさがす

説明

Vapor Grown Carbon Fiber (VGCF) is, due to its extraordinary electrical properties, a most promising filler for polymer composites, which are mostly prepared through melt mixing. However, little is known about the effects of melt mixing on the length of VGCF and the electrical conductivity of composites. Here, we have measured the length of VGCF and studied its relationship with the electrical conductivity in VGCF/polymer composites by varying melt mixing time.<br>We used a batch type twin-screw kneader, to make composites of polycarbonate (PC) and VGCF at 260°C under 450rpm of screw speed. When the mixing time became longer, the surface resistivity increased. SEM pictures of the cross sections under various mixing times were almost identical. Longer mixing times also made the complex modules G* decrease in measurements of dynamic viscoelasticity. The length measurement of VGCF showed that the average length of VGCF as received was 5.94μm. When melt mixing times increased from 7 to 600 seconds, the VGCF length decreased from 5.76 to 3.96μm. It is believed that the initial clumps of VGCF are unexpectedly easily dispersed by a very small shear strain. At larger strains, the VGCF lengths reduce causing the increase in surface reisistivity.

収録刊行物

  • 成形加工

    成形加工 17 (7), 490-496, 2005-07-20

    一般社団法人 プラスチック成形加工学会

参考文献 (30)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ