- 冨士谷 盛興
- 広島大学大学院医歯薬学総合研究科顎口腔頚部医科学講座 (保存修復学研究室)
書誌事項
- タイトル別名
-
- Adhesive Properties of Resin Bonding System to Er: YAG or CO<SUB>2</SUB> Lased Dentin
- レーザー照射象牙質面に対しレジンは本来の接着性能を発揮できるか?
この論文をさがす
説明
Laser ablation [Er: YAG (Erwin Adverl®, 60mJ/10pps), CO2 (Topal®, 1W/0.3sec)] of dentin reduces the adhesive properties of resin bonding systems. The so-called “laser-etching” might not be effective in promoting adhesion. By TEM observations of non-decalcified specimens, such morphological changes as observed in the acid-etched dentin surface could not be detected in the subsurface layer of the lased dentin. It was mechanically weakened due to the formation of structural defects and heat-denatured layer, leading to considerably lower adhesive properties. Significantly lower bond strength was obtained in the wedge-shaped defects compared with the flat surfaces. The configuration factor (C-factor) might be an important factor especially for the adhesion to lased dentin.<BR>However, high-energy laser ablation of dentin (Er: YAG: 250mJ/lOpps, CO2: 3W/0.3sec) hardly reduced the bond strength. In the subsurface layer of low-power lased dentin (Er: YAG: 60mJ/1 pps, CO2: 1W/0.3sec), TEM observations of decalcified specimens revealed that amorphous matrix substances containing denatured collagen fibers were generated (Er: YAG: 3-4μm, CO2: 1-2μm). On the other hand, in the high power-lased dentin (Er: YAG: 250mJ/1pps, CO2: 3w/0.3sec), such morphological structure that could hardly be distinguished from sound dentin (Er: YAG) or the subsurface dentin layer having both little amorphous matrix and torn collagen fibers with cross-striation (CO2) was observed. The effects of high-energy laser ablation might be limited to the superficial layer.<BR>It was concluded that laser-etching might not be effective in promoting adhesion, and that the amount of irradiation energy should be considered when evaluating the adhesive properties of resin bonding systems.
収録刊行物
-
- 日本レーザー歯学会誌
-
日本レーザー歯学会誌 17 (2), 74-80, 2006
日本レーザー歯学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679451276672
-
- NII論文ID
- 130003925132
-
- ISSN
- 21856702
- 09177450
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可