Delayed Fracture of E Glass Fiber under Water Environment
-
- KOBIKI Akira
- Graduate School of Science and Engineering, Waseda University
-
- IITAKA Seishi
- Graduate School of Science and Engineering, Waseda University
-
- SHIODA Satoshi
- Graduate School of Science and Engineering, Waseda University
-
- KAWADA Hiroyuki
- 早稲田大学理工学部
Bibliographic Information
- Other Title
-
- 水環境下におけるEガラス繊維の遅れ破壊
- ミズ カンキョウ カ ニ オケル Eガラス センイ ノ オクレ ハカイ
Search this article
Abstract
Tests for evaluating delayed fracture of an E-glass fiber were conducted under water environment. Loaded E-glass fibers were immersed in purified water, and time-to-fracture was measured. Since the delayed fracture was confirmed under the water, the moisture was the only environmental factor for the delayed fracture. The relationship between the chemical reaction and the fiber strength was evaluated for estimating moisture-absorption effect on the delayed fracture. The E-glass fiber surface was observed by XPS and AFM. These observations showed that roughness on the glass surface increased due to the moisture-absorption. Furthemore the fiber-bundle strength decreased with increasing immersion time. The results of these observations indicated that microscopic cracks accelerated the delayed fracture under the water. It is concluded that the delayed fracture of the E-glass fiber occurred by microscopic crack growth caused by moisture-absorption on the glass surface.
Journal
-
- TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
-
TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A 72 (713), 85-92, 2006
The Japan Society of Mechanical Engineers
- Tweet
Details 詳細情報について
-
- CRID
- 1390282679453716864
-
- NII Article ID
- 110004101741
-
- NII Book ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL BIB ID
- 7816450
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed