- Fatigue Strength Characteristics of Non-Combustible Mg Alloy (2nd Report, Effect of Mean Stress on Fatigue Strength)
- ナンネンセイ マグネシウム ゴウキン ノ ヒロウ キョウド トクセイ ダイ 2ホウ ヒロウ キョウド ニ オヨボス ヘイキン オウリョク ノ エイキョウ
- 2nd Report, Effect of Mean Stress on Fatigue Strength
- 第2報, 疲労強度に及ぼす平均応力の影響
この論文をさがす
抄録
Rotating bending tests and tension-compression fatigue tests on non-combustible magnesium alloy were carried out to investigate effect of mean stress on fatigue strength at N=107. The ignition point of non-combustible magnesium alloys is about 300 K higher than that of normal magnesium alloys because of calcium addition. It was clarified as follows. (1) In the range of σm=0100MPa, fatigue strength at N=107 of small hole specimens was about 30150% higher than that of small crack specimens. (2) In the range of σm>100MPa, fatigue strength at N=107 of small hole specimens decreased because of static cracks initiating around small hole at the first loading. (3) In the range of σmax<σ0.2, fatigue strength at N=107 of smooth specimens was estimated using modified Goodman diagram.
収録刊行物
-
- 日本機械学会論文集Ａ編
-
日本機械学会論文集Ａ編 74 (737), 115-121, 2008
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679454143232
-
- NII論文ID
- 110006571952
-
- NII書誌ID
- AN0018742X
-
- COI
- 1:CAS:528:DC%2BD1cXksVaku7g%3D
-
- ISSN
- 18848338
- 03875008
- http://id.crossref.org/issn/03875008
-
- NDL書誌ID
- 9359538
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可