- Effect of Loading Frequency on Fatigue Strength of Ni-Based Super Alloy
- Niキ チョウゴウキン ノ ヒロウ キョウド ニ オヨボス クリカエシ ソクド ノ エイキョウ
この論文をさがす
抄録
In order to investigate the growth mechanism of a fatigue crack of Ni-based super alloy at ultrasonic frequency, ultrasonic fatigue and rotting bending fatigue tests were carried out for Inconel 718 in ambient air and in N2 gas using plain and notched specimens and the results in both tests were compared by focusing on the effects of strain rate and environment. In ambient air, fatigue strength was higher in ultrasonic fatigue than in rotating bending fatigue in plain specimen, while the results in notched specimen were the reverse. Many transgranular cracks and cleavage like cracks were observed on the fracture surface in ultrasonic fatigue in addition to striation and transgranular facets observed in rotating bending fatigue and there was no difference in the fracture mechanism between plain specimen and notched one. Moreover, these effects of frequency on the growth mechanism of a crack in ambient air were nearly the same in N2 gas, though fatigue strength in N2 gas was higher than that in air. The increase in fatigue strength in N2 gas was mainly caused by the retardation of a crack initiation.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 72 (722), 1542-1549, 2006
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679454300416
-
- NII論文ID
- 110004837525
-
- NII書誌ID
- AN0018742X
-
- COI
- 1:CAS:528:DC%2BD2sXitVSntg%3D%3D
-
- ISSN
- 18848338
- 03875008
-
- HANDLE
- 10559/7087
-
- NDL書誌ID
- 8556311
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可