書誌事項
- タイトル別名
-
- Effect of Secondary Injection-molding Condition on the Welding Strength and Interfacial Structure of Polyoxymethylene
- POM ノ ヨウチャク キョウド ト カイメン コウゾウ ニ オヨボス 2ジ シャシュツ セイケイ ジョウケン ノ エイキョウ
この論文をさがす
説明
The relation of secondary injection-molding condition to the interfacial structure and shear welding strength of polyoxymethylene was investigated and following main results have been obtained. (1) The welding strength intensifies with increases of the secondary injection-molding speed and temperature. (2) With the increase in welding strength, the elongation to shear fracture becomes large also. The fracture mechanism of welding specimen changes from the interface debonding to the fracture with plastic deformation. (3) The higher the injection-molding speed and temperature, the molecule activation energy at the welding interface becomes high. So, the surface layer crystallization of the first molding is promoted and the trans-crystal layer is easy to be formed in the secondary molding side. It is thought to be advantageous to the improvement of welding strength. (4) Since the fracture starting point of welding specimen is at the welding interface or the surface layer of the first molding, the maximum welding strength is mainly determined by the strength of the surface layer.
収録刊行物
-
- 日本機械学会論文集Ａ編
-
日本機械学会論文集Ａ編 73 (730), 702-708, 2007
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679454933632
-
- NII論文ID
- 110006317460
-
- NII書誌ID
- AN0018742X
-
- COI
- 1:CAS:528:DC%2BD2sXhtVWis73O
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 8870005
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可