The estimation of the strain-induced martensitic transformation by using X-ray diffraction analysis of fatigue impact fracture surface and crack propagation behavior in austenitic stainless steel.

DOI Web Site Web Site 2 Citations

Bibliographic Information

Other Title
  • Ｘ線回折法によるＳＵＳ３１６衝撃疲労破面のひずみ誘起相変態量の定量化と衝撃疲労き裂伝ぱ挙動について
  • Xセン カイセツホウ ニ ヨル SUS316 ショウゲキ ヒロウ ハメン ノ

Search this article

Description

The volume fraction of strain-induced α' martensite was measured by X-ray diffraction analysis on the fracture surfaces caused by fatigue impact and standard fatigue. The volume fraction of α' martensite increased with increasing ΔK regardless of fatigue impact and standard fatigue. In standard fatigue, this volume fraction increased with increasing stress of ratio and depended on the effective stress intensity range, ΔKeff, at crack tip. If the relation between the volume fraction of α' martensite and ΔKeff in standard fatigue could be used to estimate the effective stress intensity factor, we can get the ΔKeff in fatigue impact. Thus the ΔKeff in fatigue impact was almost equal to maximum stress intensity, Kmax. The fatigue crack growth rate related to the volume fraction of α' martensite, in spite of fatigue impact, standard fatigue and stress ratio. Hence, the plastic zone formed under fatigue impact should be smaller than that from standard fatigue.

Journal

Citations (2)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top