書誌事項
- タイトル別名
-
- Fatigue fracture toughness of maraging steel.
- マルエージング コウ ノ ヒロウ ハカイ ジンセイ
この論文をさがす
説明
High-cycle fatigue tests, low-cycle fatigue tests, and static tensile tests on notched specimens of a maraging steel were conducted. not only is the fatigue fracture toughness Kfc approximately constant for high-cycle and low-cycle fatigue, regardless of applied stresses and strains, but also Kfc is approximately equal to the static fracture toughness KIC;Kfc<cong>KIC<cong>36 MPa·m1/2. Moreover, for its high tensile strength (yield stress σ0.2=2440 MPa, tensile stress σB=2490 MPa), the maraging steel has an extremely small value of KIC in comparison with other low-and medium-strength steels. Considering that the crack propagation period occupies only 20-30% of total life in high-cycle fatigue and also that the crack lengths at final fracture in low-cycle fatigue are very small in comparison with specimen size, the fatigue life prediction method on the basis of the integral of crack growth rate equation is inadequate and should not be applied to high-strength steels such as maraging steels. Instead, Kfc will be useful to predict the final fracture of maraging steels.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 54 (505), 1753-1762, 1988
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679455176320
-
- NII論文ID
- 110002377703
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
- http://id.crossref.org/issn/03875008
-
- NDL書誌ID
- 3196623
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可