圧電セラミックスにおける繰返し荷重および直流電界重畳下での疲労き裂進展挙動
書誌事項
- タイトル別名
-
- Fatigue Crack Propagation under Combined Cyclic Mechanical Loading and Electric Field in Piezoelectric Ceramics
- アツデン セラミックス ニ オケル クリカエシ カジュウ オヨビ チョクリュウ デンカイ チョウジョウ カ デ ノ ヒロウ キレツ シンテン キョドウ
この論文をさがす
説明
Fatigue crack propagation tests of PZT specimens were performed under cyclic four-point bending with and without superposition of electric fields. The specimens were poled in the longitudinal direction (PL specimens) perpendicular to the crack plane. The crack propagation rate for the case of open circuit was faster than that for the case of short circuit. The application of a negative or positive electric field parallel to the poling direction accelerated the crack propagation rate, and the amount of acceleration was larger for the case of the negative field. The change of the crack propagation rate with crack extension can be divided into three regions. In the region I, the crack propagation rate decreases with increasing crack length, and then turn to increase in the region III. In the region II, the propagation rate is nearly constant. The mechanisms of fatigue crack propagation were correlated to domain switching near the crack tip. The grain boundary fracture was predominant in the low-rate region, while transgranular fracture became abundant on the unstable fracture surface.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 72 (718), 914-921, 2006
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679455215360
-
- NII論文ID
- 110004741192
-
- NII書誌ID
- AN0018742X
-
- COI
- 1:CAS:528:DC%2BD28XovFyqsb0%3D
-
- ISSN
- 18848338
- 03875008
-
- HANDLE
- 2237/9121
-
- NDL書誌ID
- 8011343
-
- 本文言語コード
- ja
-
- 資料種別
- journal article
-
- データソース種別
-
- JaLC
- IRDB
- NDLサーチ
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可